Etude de l'effet d'un pré-écrouissage sur la durée de vie d'un acier inoxydable austénitique 304L
Résumé
This study deals with the effects of the loading history on the lifetime of 304L stainless steel (TH or CLI) in air at room température. In addition to reference tests (tension-compression) performed using "regular" cycles without any overloads until failure, fatigue-overloads tests composed of different steps applied to the same specimen have also been carried out. The results point out cyclic softening of the material, additional hardening of some virgin specimens and strong lifetime dependance on monotonous or cyclic prestraining of the material. Prestraining effects seems beneficial under stress controlled conditions but deleterious under strain controlled conditions. The tests results are analyzed in order to evaluate the changes of the elasticity modulus and the relative contributions of the isotropic and kinematic parts of the strain hardening.
Le travail est relatif aux effets de l'histoire de chargement sur la durée de vie d'un acier 304L (THY ou CLI) à l'ambiante. Des essais de traction-compression sont réalisés en deux phases : une s'intéressant au pré-écrouissage (monotone ou cyclique) du matériau, une deuxième où des cycles réguliers sont appliqués jusqu'à la rupture. Les résultats montrent un adoucissement cyclique du matériau, un durcissement cyclique secondaire sur certaines éprouvettes vierges et une grande influence du pré-écrouissage sur la durée de vie. Les effets du pré-écrouissage semblent bénéfiques en contrainte contrôlée et néfastes en déformation contrôlée. Une analyse des résultats d'essais permet d'évaluer l'évolution du module d'élasticité ainsi que les parts relatives des écrouissages isotrope et cinématique
Origine : Fichiers produits par l'(les) auteur(s)
Loading...